Bi metal liner for mud pump of 3NB1600 170mm
Bi metal liner for mud pump of 3NB1600 170mm
Bi metal liner for mud pump of 3NB1600 170mm
Bi metal liner for mud pump of 3NB1600 170mm

ae Bi metal liner for mud pump of 3NB1600 170mm

Liner Outer Sleeve: 45#forged steel, tensile strength is σb>610MPa, yield strength is σs>450MPa, ,elongation hardness is §>17%,hardness is HRC180-200 Liner Inner Sleeve: high chromium cast iron (centrifugal forged). Annealing hardness is HRC≤40. Quenching hardness is HRC59-64

Category:

aeProduct

aeMud Pump Liner

aePump bi-metal liner

Phone:+86-13292875538

Product Description

Bimetal Liners


The b-metal liner is composed of two layers and fixed tightly. The outer sleeve is forged steel with abrasion resistance, it adapts the technology of centrigugal forging;  the inner sleeve is high chromium iron with wear&corrosion resistance, after heat treatment, the hardness can reach to a lever of 62 RC.

The bimetal liners produced by us strictly control the tolerance, assure the easy installation, inner sleeve is highly polished with abrasion&corrosive resistance, can used in various bad working environment with longer service life. 

Liner Outer Sleeve: 45#forged steel, tensile strength is σb>610MPa, yield strength is σs>450MPa, ,elongation hardness is §>17%,hardness is HRC180-200
Liner Inner Sleeve: high chromium cast iron (centrifugal forged). Annealing hardness is HRC≤40. Quenching hardness is HRC59-67

Chemical Composition:C 2.8%-3.1%  Cr 26%-28%  Si 0.6%-0.9%  Mn 0.5%-1% Mo 0.5%-0.8% S , P <0.05%;